Glass-filled SLA resin for highly stiff, precise parts with a smooth matte surface. Suitable for evaluating fixtures, tooling and dimensionally stable prototypes.
High stiffness means limited flexibility. Elastic snap fits or repeated substantial bending require evaluation of other materials.
The properties below apply to V1 FLRG1001 under the stated test conditions. The Form 4 formulation FLRG1011 is separate. Printer, formulation and post-processing are confirmed before production.
65 MPa · V1 FLRG1001; Form 3, 100 µm; UV post-cure 60 min / 70 °C; without media blasting; ASTM D638-14
Tensile modulus
10 GPa · V1 FLRG1001; Form 3, 100 µm; UV post-cure 60 min / 70 °C; without media blasting; ASTM D638-14
Elongation at break
1 % · V1 FLRG1001; Form 3, 100 µm; UV post-cure 60 min / 70 °C; without media blasting; ASTM D638-14
Flexural modulus
9 GPa · V1 FLRG1001; Form 3, 100 µm; UV post-cure 60 min / 70 °C; without media blasting; ASTM D790-15
Heat deflection temperature at 0.45 MPa
163 °C · V1 FLRG1001; Form 3, 100 µm; UV post-cure 60 min / 70 °C; without media blasting; ASTM D648-16
Source review: 2026-10-06
Limitations and post-processing
Suitability depends on geometry, orientation, print profile and material condition. Drying, annealing, or washing and post-curing are material- and profile-specific. Material data do not certify a part.